How To Remove Dlc Coating
NJBillK
Custom Leather and Fixed Blade modifications.
- #5
The DLC bond can be weakened with a soak in hydrogen peroxide. I forget where I read it, merely it worked for my ZT770cfM4.
I pulled the blade out of my knife and soaked it in a glass filled with hydrogen peroxide for one.5 - 2 hours. I kept checking on it, simply it simply sabbatum there and every now and and so information technology would release a gas bubble or two. Later on I striking it with some 2k SiC sandpaper under running water. That left me with the impromptu blackwash yous meet below.
With how the ridges polished up after a infinitesimal or and then of sandpaper, I would think the soaking is close to what was needed.
I sanded by manus and without a block and then I would merely soften it all around and polish the highs.
If you were to use a solid capitalist, I am sure yous could go almost all of it off relatively easily.
NJBillK
Custom Leather and Stock-still Blade modifications.
- #7
Not that I was enlightened of, but then once again I did resharpen it since it was due...
It did not affect the pin area at all. I brought that up to 5k, the polished information technology with my strop.
NJBillK
Custom Leather and Stock-still Blade modifications.
- #12
I recall the soak did aid. I tried striking it with the 2k prior to the soak to see if there would exist much of a difference. It scuffed it upward, but didn't remove anything meaning.
The bubbles were intermittent from random spots on the blade. They were generated in plenty time that I could wait over and watch one or two rise. I wouldn't say they were abiding stream, just they were definitely existence generated from some grade of reaction.
Thanks for the compliments.
NJBillK
Custom Leather and Fixed Blade modifications.
- #16
Wowbagger
Lol.
Information technology is actually a bit rougher than i thinks on skin too.
The fashion it goes most "cleaning" a wound is by eating abroad at the surface slightly to reveal "fresher" tissue. This is particularly beneficial when you lot are putting some ointment (triple bac, bacitracin, et al) on it to expedite healing. Which is more often than not used in a dirty cut or a scrape later a decent cleaning by ways of picking the larger bits out, then scrubbing and flushing it out.
Oh, a word of feel, the scrubbing flake sucks the most.
If yous tin can't tell, I have fallen down a lot.
NJBillK
Custom Leather and Fixed Blade modifications.
- #19
I've contacted you about that in the past...but didn't end upwards trying it on the knife I was focused on at the time.
Looking at the quoted statement, I find myself wondering if the "pre-sanding" is a primal pace. Would the same effect have been attained without it, or might the unmarred DLC have withstood the claiming? I've still got my 0770cfm4 sitting new in the box...perchance I'll practice some experimenting one rainy twenty-four hours this calendar week.
I only sanded a small portion. The way that I looked at it, why sand the whole thing if a pocket-size spot would be easier and requite me the information I sought.
It was in a higher place the flipper tab on the pile (lock) side, then if information technology was significantly different, it wouldn't event the look too drastically in a spot that was immediately visable.
I was primarily curious nigh how hard information technology would be to sand off. Simply I didn't want an overly stripped expanse the size of a fingerprint on the secondary when a more than inconspicuous spot was available.
Final edited:
How To Remove Dlc Coating,
Source: https://www.bladeforums.com/threads/removing-dlc.1502300/